Grade 1 Titanium Round Rod For Architecture

GR1 pure titanium Rod , as a unique metal material, with its excellent performance, shows a wide range of application prospects in many fields.The main component of GR1 titanium bar is titanium, a silver-white transition metal, with high strength, low density and good corrosion resistance and other characteristics. This metal is resistant to a wide range of strong acids and bases at room temperature, demonstrating its exceptional durability.

Get Detailed Technical Data

 

Chemical Composition (Weight % - Typical)

Element	Content (Max. %)
Titanium (Ti)	Balance (≥ 99.5%)
Nitrogen (N)	0.03
Carbon (C)	0.08
Hydrogen (H)	0.015
Iron (Fe)	0.20
Oxygen (O)	0.18
Other Elements, each	0.10
Other Elements, total	0.40

 

Grade 1 Titanium of Mechanical Properties

Hardness, Brinell	120	120	annealed
Hardness, Knoop	132	132	Estimated from Brinell.
Hardness, Rockwell B	70	70	annealed
Hardness, Vickers	122	122	Estimated from Brinell.
Tensile Strength, Ultimate	240 MPa	34800 psi
Tensile Strength, Yield	170 - 310 MPa	24700 - 45000 psi
Elongation at Break	24 %	24 %
Reduction of Area	35 %	35 %
Modulus of Elasticity	105 GPa	15200 ksi	In Tension
Compressive Modulus	110 GPa	16000 ksi
Poisson's Ratio	0.37	0.37
Charpy Impact	310 J	229 ft-lb	V-notch
Shear Modulus	45 GPa	6530 ksi

1. Curtain wall system: In high-rise buildings and public buildings, Grade 1 titanium rods are often used to make curtain wall support structures and connectors.
2. Decorative components: Grade 1 titanium rods can be used to make decorative components of buildings, such as railings, handrails, sculptures, etc.
3. roof and wall support: grade 1 titanium round bar can be used as roof and wall support structure, especially in the seaside or humid areas, can effectively resist corrosion.

 

Capability	Key Processes & Expertise
Precision Machining	CNC milling, turning, drilling & tapping. Utilizing sharp tooling, optimized feeds/speeds, and dedicated coolants to overcome GR1's "gummy" nature and achieve tight tolerances.
Forming & Fabrication	Cold rolling, deep drawing, press brake bending, hydroforming. Leveraging GR1's exceptional ductility for complex shapes with controlled springback.
Welding & Joining	High-purity argon GTAW (TIG) welding, laser welding. Full-trailing gas protection for oxide-free, corrosion-resistant welds. Post-weld stress relieving available.
Cutting & Blanking	High-definition plasma cutting, waterjet cutting, laser cutting. Delivering clean edges with minimal heat-affected zone for superior downstream processing.
Surface Finishing	Mechanical polishing (to mirror or satin), abrasive blasting, pickling (to ASTM/medical standards), passivation. Preparing surfaces for final use or coating.

Get Free Sample & Evaluation

 

What is GR1 Titanium?
GR1 (Grade 1) is commercially pure, unalloyed titanium with a minimum titanium content of 99.5%. It is the most ductile and corrosion-resistant grade among pure titanium alloys, making it ideal for applications where forming and corrosion resistance are critical.

 

Can GR1 titanium be welded?
Yes, GR1 has excellent weldability. Gas Tungsten Arc Welding (GTAW/TIG) with high-purity argon shielding is the standard method. Proper cleaning and shielding are essential to prevent oxidation and maintain corrosion resistance.

 

Does GR1 titanium work harden?
Yes, like most pure metals, GR1 can work-harden during cold forming or machining. Intermediate annealing may be required for severe deformation operations to restore ductility and prevent cracking.

 

Can GR1 be heat-treated for higher strength?
No, GR1 is a non-heat-treatable alloy. Its strength is derived from cold working. Annealing is the only thermal process used to relieve stresses and soften the material after cold working.

 

Is GR1 titanium suitable for medical implants?
Yes, GR1 is widely used for permanent and temporary medical implants (e.g., bone plates, screws, cranial meshes) due to its excellent biocompatibility, corrosion resistance in bodily fluids, and non-toxic nature.

 

How does GR1 compare to GR2 titanium?
GR1 has lower strength but higher ductility and corrosion resistance than GR2. GR2 is more widely used for general-purpose applications, while GR1 is chosen for the most demanding corrosive environments or where severe forming is required.

 

Product Form	Available Shapes / Types	Common Grades	Typical Dimensions (Range)	Standard Specifications
Titanium Tube & Pipe	- Seamless Pipe - Welded Pipe - Heat Exchanger Tubes (U-Tube, Straight) - Hydraulic & Instrumentation Tubing	GR1, GR2, GR7, GR9, GR12, GR5 (Ti-6Al-4V)	- OD: 1/8" to 12" (3mm - 325mm) - Wall Thickness: 0.028" to 1.0" (0.7mm - 25mm) - Length: Up to 20ft (6m) standard, custom lengths available	ASTM B337, B338, B861, B862 ASME SB337, SB338
Titanium Sheet & Plate	- Cold Rolled Sheet - Hot Rolled Plate - Checker Plate / Tread Plate	GR1, GR2, GR5, GR7, GR9, GR12	- Sheet Thickness: 0.016" to 0.187" (0.4mm - 4.7mm) - Plate Thickness: 0.187" to 4" (4.7mm - 100mm)+ - Width: Up to 60" (1500mm) - Length: Up to 240" (6000mm)	ASTM B265 ASME SB265
Titanium Bar & Rod	- Round Bar - Hex Bar - Square Bar - Forged Bar - Centerless Ground Bar	GR1, GR2, GR5, GR7, GR9, GR12	- Round Bar Diameter: 0.125" to 12" (3mm - 300mm) - Hex/Square: 0.125" to 4" (3mm - 100mm) - Length: Random, cut-to-length, or coils (small diameters)	ASTM B348 ASME SB348
Titanium Wire	- Coiled Welding Wire - Straight Length Wire - Spring Wire - Fastener Wire	GR1, GR2, GR5 (ELI for medical), GR7	- Diameter: 0.010" to 0.25" (0.25mm - 6.35mm) standard - Spool Weight: Standard 5lb, 10lb, 25lb spools; custom packaging available	ASTM B863, F67 (for medical)
Titanium Strip & Foil	- Cold Rolled Strip (Coil) - Precision Foil - Shim Stock	GR1, GR2, GR5	- Thickness (Strip): 0.004" to 0.125" (0.1mm - 3.1mm) - Thickness (Foil): 0.0005" to 0.004" (0.012mm - 0.1mm) - Width: Up to 24" (600mm)	ASTM B265 (strip/foil)

Discuss Your Project Requirements

 

Our factory is equipped with advanced production machinery, including CNC machining centers (3 to 5-axis), high-precision tube mills, cold rolling mills, automated wire drawing lines, and CNC-controlled cutting systems (laser, waterjet, and plasma). We maintain a Class 100,000 clean workshop for medical and aerospace production, supported by argon-protected welding bays, vacuum annealing furnaces, and full-spectrum quality testing labs with CMM, spectrometer, and ultrasonic testing equipment. From raw material to finished product, every step is executed under controlled conditions to ensure dimensional accuracy, metallurgical integrity, and compliance with international standards.

 

Our standard packaging protocol includes multiple protective layers tailored to the specific product form and customer requirements. All materials are first cleaned, dried, and wrapped with VCI (Vapor Corrosion Inhibitor) paper or PE film to prevent oxidation and surface contamination. Products are then securely bundled and cushioned with waterproof corrugated paper and edge protectors. Finished bundles are placed in plywood crates, heavy-duty cardboard boxes, or sealed in moisture-proof PVC film on pallets, with clear, durable labeling for handling and identification. For international sea freight, we offer IPPC-certified fumigation wooden cases or seaworthy export crates, ensuring your order arrives safely and in ready-to-use condition, no matter the destination.

Get Fast Quote & Logistics Plan

 

Hot Tags: grade 1 titanium round rod for architecture, China grade 1 titanium round rod for architecture manufacturers, suppliers, factory, Nickel 200 201 Seamless Alloy Tubes, Nickel Alloy Thick walled Pipe, Gr4 Titanium Pipe, Titanium Round Wire, Titanium Alloy Foil, pure Gr7 titanium sheet